中文摘要: 本文采用热处理工艺和表面活性剂对石墨表面进行改性处理， 采用氢还原包覆工艺制备镍包石墨粉末， 对
比了不同石墨热处理工艺和表面活性剂的添加对镍包石墨粉末表面形貌和物理性能的影响。 研究表明 , 在热处理
温度 500℃， 采用醇类活性剂表面处理石墨后， 通过加压氢还原工艺制备的镍包石墨粉末具有较好的表面包覆完
整性和优异的粉末松装密度和流动性。
Abstract:The graphite surface was modified by heat treatment process and surfactant, and nickel-coated graphite
powder was prepared by hydrogen reduction coating process. The effects of different graphite heat treatment
processes and surfactant addition on the surface morphology and physical properties of nickel-coated graphite
powder were compared. The results showed that when the graphite was treated with alcohol-based surfactants at
the heat treatment temperature of 500℃ , the nickel-coated graphite powder prepared by the process of pressurized
hydrogen reduction exhibited good surface coating integrity and excellent powder packing density and fluidity.
文章编号： 中图分类号： 文献标志码：
基金项目:
| 作者 | 单位 |
| 冀国娟 | 矿冶科技集团有限公司；特种涂层材料与技术北京市重点实验室；北京市工业部件表面强化与修复工程技术研究中心 |
| 李振铎 | 矿冶科技集团有限公司；特种涂层材料与技术北京市重点实验室；北京市工业部件表面强化与修复工程技术研究中心 |
| 程旭莹 | 矿冶科技集团有限公司；特种涂层材料与技术北京市重点实验室；北京市工业部件表面强化与修复工程技术研究中心 |
引用文本：
冀国娟,李振铎,程旭莹.石墨表面改性工艺对镍包石墨粉末性能影响研究[J].热喷涂技术,2020,12(2):41-46.
GuojuanJi,Zhenduo Li,Xuying Cheng.The Study of the Graphite Surface Modifcation Effecton the Properties of Nickel-coated Graphite Powder[J].Thermal Spray Technology,2020,12(2):41-46.
冀国娟,李振铎,程旭莹.石墨表面改性工艺对镍包石墨粉末性能影响研究[J].热喷涂技术,2020,12(2):41-46.
GuojuanJi,Zhenduo Li,Xuying Cheng.The Study of the Graphite Surface Modifcation Effecton the Properties of Nickel-coated Graphite Powder[J].Thermal Spray Technology,2020,12(2):41-46.