激光功率对 SLM 制备非晶合金成形及晶化的影响
(矿冶科技集团有限公司 北京市工业部件表面强化与修复工程技术研究中心 特种涂层材料与技术北京市重点实验室)
Effect of Laser Power on Forming Quality and Crystallization ofAmorphous Alloy Prepared by SLM
(BGRIMM Technology Group,Beijing Engineering Technology Research Center of Surface Strengthening and Repairing of Industry Parts,Beijing Key Laboratory of Special Coating Material and Technology)
摘要
图/表
参考文献
相似文献
本文已被:浏览 330次   下载 1634
    
中文摘要: 非晶合金以其独特的原子排列和优异的性能引起人们的广泛关注, 但由于尺寸、 晶化等问题严重限制了 实际工程中的应用, 激光增材制造技术具有高升温 - 冷却速率和逐点熔融沉积的特点, 为制备非晶合金提供了新 思路。 本文采用选择性激光熔融成型技术制备 Zr50Ti5Cu27Ni10Al8 非晶合金。 对制备出的样品的成分和组织结构进 行了表征。 结果表明, 样品主要由非晶相构成, 晶化主要发生在热影响区叠加区。 随激光功率的降低, 晶化区面 积和晶化颗粒数量减少。 但过低的功率会产生未熔合缺陷和裂纹, 严重影响非晶合金的成形质量和非晶率。
中文关键词: 激光选区熔化  非晶合金  晶化
Abstract:Amorphous alloys have attracted extensive attention due to their unique atomic arrangement and excellent properties. However, the size, crystallization and other problems may seriously limit the engineering application. Laser additive manufacturing technology has the characteristics of high heating, cooling rate and point by point melting deposition, which provides a new idea for the preparation of amorphous alloys. Zr50Ti5Cu27Ni10Al8 amorphous alloy was prepared on the surface of pure zirconium substrate by selective laser melting technology. The composition and structure of the samples were characterized. The results showed that the samples are mainly composed of amorphous phase, and the crystallization mainly occurs in the superimposed zone of heat affected zone. With the decrease of laser power, the area of crystallization zone and the number of crystallization particles decreased. However, if the laser power is too low, there will be non-fusion defects and cracks, which will seriously affect the forming quality and amorphous rate of amorphous alloy.
文章编号:     中图分类号:TG174.4    文献标志码:
基金项目:
引用文本:
孟玲,陈星,杜开平.激光功率对 SLM 制备非晶合金成形及晶化的影响[J].热喷涂技术,2021,13(1):60-64.
Meng Lin,Chen Xing,Du Kaiping.Effect of Laser Power on Forming Quality and Crystallization ofAmorphous Alloy Prepared by SLM[J].Thermal Spray Technology,202113(1):60-64.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299752,9751,9758

杂志文章

杂志信息

联系我们

电话:010-63299752,9751,9758

Email:rptjs@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号