叶俊华,陈凌云,陈新悦,程小红,杨亚飞,张川.基于正交试验的等离子喷涂 NiAl 和 NiCrAl 涂层工艺研究[J].热喷涂技术,2022,14(1):78~84.
基于正交试验的等离子喷涂 NiAl 和 NiCrAl 涂层工艺研究
Research on Plasma Spraying NiAl and NiCrAl Coatings Process Based on Orthogonal Experiment
  
DOI:DOI 10.3969/j.issn.1674-7127.2022.01-010
中文关键词:  等离子喷涂  镍铝涂层  镍铬铝涂层  正交试验
英文关键词:Plasma spray  NiAl coating  NiCrAl coating  Orthogonal experiment
基金项目:
                 
作者单位
叶俊华 成都航利(集团)实业有限公司
陈凌云 成都航利(集团)实业有限公司
陈新悦 成都航利(集团)实业有限公司
程小红 成都航利(集团)实业有限公司
杨亚飞 成都航利(集团)实业有限公司
张川 成都航利(集团)实业有限公司
摘要点击次数: 4
全文下载次数: 4
中文摘要:
      基于正交试验研究了等离子喷涂 NiAl 和 NiCrAl 涂层过程中结合强度与等离子喷涂参数之间的响应关系, 分析了涂层显微特征的影响因素并据此优化了工艺参数。结果表明,影响 NiAl 涂层结合强度的因素主次顺序为 氢气流量、氩气流量、电流、喷涂距离,影响 NiCrAl 涂层结合强度的因素主次顺序为喷涂距离、氩气流量、电 流、氢气流量,工艺优化能够显著改善 NiAl 和 NiCrAl 涂层的显微特征和性能。NiAl 涂层的工艺范围为氩气流 量 110~120 SCFH,氢气流量 20~25 SCFH,电流 600~610 A,喷涂距离 130~140 mm,结合强度均在 30 MPa 以上, 最大值为 33 MPa。NiCrAl 涂层的工艺范围为氩气流量 120~130 SCFH,氢气流量 25~30 SCFH,电流 610~620 A, 喷涂距离 130~140 mm,最大结合强度为 43.6 MPa。
英文摘要:
      The response relationship between bonding strength and plasma spraying parameters in the process of plasma spraying NiAl and NiCrAl coatings was studied by the orthogonal experiment. The influencing factors of coating microstructure were analyzed, and the process parameters were optimized. The results showed the factors that affect the bonding strength of NiAl coating were hydrogen flow, argon flow, current, spraying distance. Meanwhile, the factors of the NiCrAl coating were spraying distance, argon flow, current, hydrogen flow. The microstructure and performance of NiAl and NiCrAl coatings can be significantly improved by process optimization. The optimized process range of NiAl coating was argon flow rate 110~120 SCFH, hydrogen flow 20~25 SCFH, current 600~610 A, and spraying distance 130~140 mm, the bonding strength was all above 30 MPa, and the maximum value was 33 MPa. At the same time, the optimized process range of NiCrAl coating was argon flow 120~130 SCFH, hydrogen flow 25~30 SCFH, current 610~620 A, and spraying distance 130~140 mm, the maximum bonding strength was 43.6 MPa.