铜铝 / 镍石墨封严涂层高温可磨耗性能研究
(成都航利实业集团有限公司)
Study On High Temperature Abradabilityof CuAl/Ni Graphite Sealing Coatings
摘要
图/表
参考文献
相似文献
本文已被:浏览 298次   下载 400
    
中文摘要: 采用高温高速可磨耗试验机, 在温度为 450 ℃, 刮擦线速度为 350 m/s, 进给速率分别为 10 μm/s、 50 μm/s、 100 μm/s 条件下, 对铜铝 / 镍石墨封严涂层进行了高温高速可磨耗实验; 并利用体式显微镜、 扫描电镜、 能谱对 试样刮擦前后的微宏观形貌进行了分析。 同时, 对试样高温高速磨耗过程中叶尖与涂层之间的作用力和磨损质量 进行了分析。 研究结果表明, 涂层试样经磨削后部分试样表面会出现麻坑, 叶尖表面有涂层转移附着; 涂层粘附 转移现象随着进给速率的增加而减少; 叶尖与涂层之间的最大切向力、 最大径向力、 平均径向力和平均切向力均 随着进给速率的增加而增加, 涂层磨损质量随进给速率的增加而减少。 叶片磨损质量和叶尖磨损比值分析表明, 叶尖与对应的铜铝 / 镍石墨封严涂层构成的体系可磨耗性能匹配性较好。
Abstract:The high temperature and high speed abrasion test was conducted on the CuAl/Ni-graphite sealing coating with a speed of 350 m/s, temperature at 450 ℃ and the incursion rate of 10 μm/s, 50 μm/s, 100 μm/s respectively. The macrostructures and microstructures were analyzed with T-type microscope, SEM, EDS. At the same time, the force between the blade tip and the coating, the wear quality during high temperature and high speed wear of the sample was investigated. The results showed that after grinding, the pits appeared on the surface of some coated samples, and the adhesive transfer layer also occurred on the top of the tip. The transfer layer decreased with the increase of feed rate. The maximum tangential force, the maximum radial force, the average radial force and the average tangential force between the tip and the coating increased with the increase of the feed rate. The wear mass of coating decreased with the increase of feed rate. IQR and IDR analysis indicated that the abrasion performance of the system composed of blade tip and copper-Al/nickel-graphite sealing coating was well matched.
文章编号:     中图分类号:TG174.4    文献标志码:
基金项目:
引用文本:
李俊辰,罗奎林,陈明旭,钱磊,刘畅.铜铝 / 镍石墨封严涂层高温可磨耗性能研究[J].热喷涂技术,2023,15(1):52-60.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
010-63299752,9751,9758

杂志文章

杂志信息

联系我们

电话:010-63299752,9751,9758

Email:rptjs@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号